Prong Buttons common problems and solutions You Know

Summed up based on years of experience specializing in the production and sale of buttons, most of the customers are due to insufficient experience during transfer machine. But how can it be adjusted most standards? That is, after prong buckle hit the clothes, nails and claws between male (female) is not inserted into buckle, but buttons and no deformation was the best. Then how in Ipomoea buckle he did not play in the clothes seen its quality? There are also several ways you can reference. First, the copper thickness. Not all products have quality to determine the thickness, different clothes with different thicknesses. Second, the male and the female. Male and female engaging after deduction not hard to poke, poke at that moment after closing are crisp sound, then this is a good quality prong buckle. But this will have to exclude the customer requirements of male and female buckle bite deliberately transferred to a low situation. Reduce the degree of engagement

After deduction of the mother has less elastic, it can not very crisp sound. Based on the above I listed the following 11 questions and the corresponding solutions.

⒈ play up there tight loose buckle force there. A, if before playing OK, then hit the button to adjust the machine too. B, may be associated with other manufacturers is not the same product mix. C, the mold has a problem.

⒉ destructive enough, easy to fall off. A, button machine shut height adjustment is not good. B, cloth or thick claws long enough. C, claw material is too thin, the hardness is not enough.

⒊ dew claws have to play up the situation. A, button machine up and down is not perpendicular to the eccentric. B, male and female buckle edging too low or too narrow, the gap paw enough bits (not playing by hand before detection). C, if the jaw faces this has happened, it may be too long due to the claw, use short claws.

⒋ paws broken off when the play button. A, button machine tuning is too low. B, claws too high hardness, not easy to bend. C, plating problems, make the claws hard and brittle, especially stripping (after plating has good color, plating again another color) is likely to cause. D, male and female buckle on the back of the space, the shape is not good enough, not enough to make the claw feet and broken bits.

⒌ engaging force after repeated occlusion of loose change or not snap to use. A, button material is too thin, elastic recovery is not enough. B, male and female buckle manufacturing process is not up to standard.

Male and female buckle surface dew point ⒍ play button, unsightly. A, male and female buckle material is too thin or too thick claw materials do not match. B, playing with the male and female mold surface shape buckle discrepancies.

⒎ playing pearlescent surface Ipomoea buckle sometimes rupture sometimes OK. A, button machine up and down axis is not locked, let the machine play button closure highly consistent. B, pearl face with thick or thin surface curvature of different shapes. C, mold concave surface curvature of the bead position does not match.

When ⒏ packed side surface indentation, seriously affecting the quality. A, button face is too thin to withstand the force is not enough. B, button machine adjusted too low. C, play mode button shape and surface is not met, you can change the mold. D, when the play button under the center of the die can not pay attention to debris.

When painting prong buckle ⒐ playing surface, peeling paint. A, play with the shape of the mold surface shape of the jaw discrepancies. B, paint quality is not good, general-name paint adhesion is poor. C, before spray degreasing is not clean.

D, if iron, attention problems not too high, so as not to damage the paint.

After the play button ⒑ male and female buckle buckle no force, but not before a good fight. A, button machine adjustment is not correct, the button has been deformed. B, not die.

After ⒒ play button after repeated engaging, fabric surface crack at the claw ring. A, button machine calibration is too low, the fabric extrusion rupture. B, claw ring edge burr, to cut them off.